Assessment of radioactivity concentration for building materials used in Babadogo Estate, Nairobi City County, Kenya.

Natural radioactive materials in certain conditions can get to hazardous radiological level. The aim of the present work was to evaluate the natural activity concentration from sampled building materials collected from different locations in Babadogo Estate within Nairobi City County. The analysis done using gamma ray spectrometer, which was put into action for spectral data acquisition and then analysis. The activity concentration levels of 238U, 232Th and 40K for the selected samples of building materials was measured by the use of gamma ray spectrometry method. The analyzed data compared with the standard acceptable values. The activity concentration in 40K varied from 55 ± 3 to 2647 ± 132 Bq kg-1, giving an average (sum of all values divided by 33) value of 831 ± 42 Bq kg-1; 238U varied from 39 ± 2 to 3602 ± 180 Bq kg-1, giving average figures of 378 ± 19 Bq kg-1 and 232Th ranged from 5.000 ± 0.300 to 4213 ± 211 Bq kg-1, giving average figure of 290 ± 15 Bq kg-1. The calculated average figures for activity concentration surpassed the world average values of 420, 33 and 45 Bq kg-1 in 40K, 238U and 232Th, respectively.

Charge transport mechanism in thin cuticles holding nandi flame seeds.

Metal-sample-metal sandwich configuration has been used to investigate DC conductivity in 4 mum thick Nandi flame [Spathodea campanulata P. Beauv.] seed cuticles. J-V characteristics showed ohmic conduction at low fields and space charge limited current at high fields. Charge mobility in ohmic region was 4.06 x 10(-5) (m(2)V(-1)s(-1)). Temperature-dependent conductivity measurements have been carried out in the temperature range 320 K < T > 450 K. Activation energy within a temperature of 320 K-440 K was about 0.86 eV. Variable range hopping (VRH) is the main current transport mechanism at the range of 330-440 K. The VRH mechanism was analyzed based on Mott theory and the Mott parameters: density of localized states near the Fermi-level N(E(F)) approximately 9.04 x 10(19) (eV(-1)cm(-3)) and hopping distance R approximately 1.44 x 10(-7) cm, while the hopping energy (W) was in the range of 0.72 eV-0.98 eV.